HONGCHENG
Produce name | Raw MDF board |
Size | 1220mmx2440mm |
Thickness | 2.0-25mm |
Glue | E0/E1/WBP/Melamine |
Core | Poplar,pine,combi |
Moisture | 4%-8% |
Surface | plain |
Density | 730-860kg/CBM |
Density tolerance | +/-1.0% |
Elastic stress | ≥3500Mpa |
Grab-screw holding | surface≥1000N,edge≥800N |
Bending strength | ≥20Mpa |
Water absorption | ≤ 10% |
Surface bond strength | ≥ 1.2Mpa |
Swelling | ≤10% |
Measurement stabilty | ≤0.8% |
Formaldehyde releasing | E0≤ 3 mg/100g, E1≤ 9mg/100g, E2≤ 30mg/100g |
Application | MDF is man-made board,adopting good logs as raw material, and mixed with urea-formaldehyde resin and other glues.Widely used indoor,furniture manufacturing,household decoration, wall panels,etc |
Advantages | The advantages of mdf are as follows: 1.It is not easy to transform and wrap 2.Close to natural to wood and better than orginal one, without the faults of natural woods 3.Good mechnical processing performacerocessing 4.Flat surface,so it is easy for secondary process |
Produce name | Raw MDF board |
Size | 1220mmx2440mm |
Thickness | 2.0-25mm |
Glue | E0/E1/WBP/Melamine |
Core | Poplar,pine,combi |
Moisture | 4%-8% |
Surface | plain |
Density | 730-860kg/CBM |
Density tolerance | +/-1.0% |
Elastic stress | ≥3500Mpa |
Grab-screw holding | surface≥1000N,edge≥800N |
Bending strength | ≥20Mpa |
Water absorption | ≤ 10% |
Surface bond strength | ≥ 1.2Mpa |
Swelling | ≤10% |
Measurement stabilty | ≤0.8% |
Formaldehyde releasing | E0≤ 3 mg/100g, E1≤ 9mg/100g, E2≤ 30mg/100g |
Application | MDF is man-made board,adopting good logs as raw material, and mixed with urea-formaldehyde resin and other glues.Widely used indoor,furniture manufacturing,household decoration, wall panels,etc |
Advantages | The advantages of mdf are as follows: 1.It is not easy to transform and wrap 2.Close to natural to wood and better than orginal one, without the faults of natural woods 3.Good mechnical processing performacerocessing 4.Flat surface,so it is easy for secondary process |